Please report any queries concerning the funding data grouped in the sections named "Externally Awarded" or "Internally Disbursed" (shown on the profile page) to your Research Finance Administrator. Your can find your Research Finance Administrator at http://www.ucl.ac.uk/finance/research/post_award/post_award_contacts.php by entering your department
Please report any queries concerning the student data shown on the profile page to:

Email: portico-services@ucl.ac.uk

Help Desk: http://www.ucl.ac.uk/ras/portico/helpdesk
Publication Detail
3D printed Ni/Al2O3 based catalysts for CO2 methanation - a comparative and operando XRD-CT study
Abstract
© 2019 Elsevier Ltd. Ni-alumina-based catalysts were directly 3D printed into highly adaptable monolithic/multi-channel systems and evaluated for CO2 methanation. By employing emerging 3D printing technologies for catalytic reactor design such as 3D fibre deposition (also referred to as direct write or microextrusion), we developed optimised techniques for tailoring both the support's macro-and microstructure, as well as its active particle precursor distribution. A comparison was made between 3D printed commercial catalysts, Ni-alumina based catalysts and their conventional counterpart, packed beds of beads and pellet. Excellent CO2 conversions and selectivity to methane were achieved for the 3D printed commercial catalyst (95.75% and 95.63% respectively) with stability of over 100h. The structure-activity relationship of both the commercial and in-house 3D printed catalysts was explored under typical conditions for CO2 hydrogenation to CH4, using operando 'chemical imaging', namely X-Ray Diffraction Computed Tomography (XRD-CT). The 3D printed commercial catalyst showed a more homogenous distribution of the active Ni species compared to the in-house prepared catalyst. For the first time, the results from these comparative characterisation studies gave detailed insight into the fidelity of the direct printing method, revealing the spatial variation in physico-chemical properties (such as phase and size) under operating conditions.
Publication data is maintained in RPS. Visit https://rps.ucl.ac.uk
 More search options
UCL Researchers
Author
Dept of Chemistry
University College London - Gower Street - London - WC1E 6BT Tel:+44 (0)20 7679 2000

© UCL 1999–2011

Search by